Purpose Of Ceramic Fiber Board in Wood Stove

Name: China Customized Purpose Of Ceramic Fiber Board in Wood Stove Suppliers, Factory - Wholesale Price - Soaring Universe Refractory
Brand: SUNTHERM
SKU: 179454258

Purpose of ceramic fiber board in wood stove, temperature resistance up to 1100 ℃, heat insulation, energy saving and pollution-free.

Send Inquiry

SUNTHERM PRODUCT CATALOG

Description

Product Introduction

Purpose of ceramic fiber board in wood stove,Ceramic fiber board is aluminum silicate fiber board, a board made of refractory materials. Even after heating, it also maintains good mechanical strength. Compared with fiber blanket and felt, this product is a rigid fiber insulation product with supporting strength. The main raw materials are pyrogem and aluminum oxide powder.

In addition to the excellent properties corresponding to bulk ceramic fiber cotton, ceramic fiber board has hard texture, excellent toughness and strength, and excellent wind erosion resistance. It has the advantages of non expansion, light weight, convenient construction, and can be cut and bent at will. It is an ideal energy-saving material for various combustion furnaces, kilns, pipelines and other insulation equipment.

1. High compressive strength and long service life;

2. Low thermal capacity and low thermal conductivity;

3. Non brittle material, good toughness;

4. Accurate size and good flatness;

5. Easy to cut and install, convenient for construction;

6. Excellent wind erosion resistance;

7. Continuous production, uniform fiber distribution and stable performance.

At present, the ceramic fiber heating plate compressed from the ceramic fiber blanket is gradually becoming the preferred refractory for the lining insulation of modern industrial kilns due to its high temperature resistance, easy construction and other advantages. Because the kilns need stable heating elements, the ceramic fiber heating plate is famous for its stability, and the manufacturing cycle of the ceramic fiber heating plate is also relatively long, This is because the process is as follows: the blowing fiber (short and fine fiber, easy to break and mix) is used as the raw material of ceramic fiber board, a certain proportion of binder and filler grade additives are added, and the slurry is fully dispersed into slurry in the slurry mixing tank through the beater. Pump into the forming pool and mix with compressed air. Put the mold into the forming pool, and use the principle of vacuum pumping to make the fiber slurry adsorb on the mold. Accurately control the adsorption time, vacuum dewater and demould the wet fiber material, and place it on a tray and send it to the drying oven for drying for 10-24 hours. The size of the dried fiberboard is precisely controlled by a special grinding machine and an edge cutting machine.

Product Parameter

Item			STD	HP		HA		ZA	HTZ
Classification Temp (℃)			1260 (2300F)	1260 (2300F)		1360 (2480F)		1360 (2480F)	1430 (2600F)
Working Temp (℃)			≤1050	≤1100		≤1200		≤1200	≤1350
Color			Pure White	Pure White		Pure White		Pure White	Pure White
Bulk Density (Kg/m3)			280---600	280---600		280---600		280-600	280---600
Permanent Linear change (%)			1000℃X24h≤ -3	1100℃X24h≤ -3		1200℃X24h≤ -3		1200℃X24h≤ -3	1350℃X24h≤ -3
ThermalConductivity(w/m.k)		200C	0.074	0.055		0.078	0.078		0.078
		400C	0.092	0.073		0.102	0.102		0.102
		500C	0.103	0.086		0.116	0.116		0.116
		600C	0.127	0.105		0.12	0.12		0.12
Tensile Strength (Mpa)			0.50	0.50	0.50			0.5	0.50
Chemical Composition (%)	AL2O3		45—46	47—49	52—55			45-46	39—40
	AL2O3+SIO2		97	99	99			-	－
	AL2O3+SIO2+ZrO2		－	－	－			99	99
	ZrO2		－	－	－			5-7	15—17
	Fe2O3		≤ 1.0	≤0.2	≤0.2			≤0.2	≤0.2
	Na2O+K2O		≤ 0.5	≤ 0.2	≤ 0.2			≤0.2	≤ 0.2
Size(mm)			Length:600 & 900 & 1200; Width:300 & 600 & 1000 & 1200 Thickness: 3-100; As customers ‘requirements.
Package			Cartons or as customer’s requirement.
Certificate			CE,ISO9001-2008; ISO14001-2004,SGS, ROHS,SASO, REACH